产品详情
K224-G6PA6
荷兰试模具料DSMK224-G6PA6
| 热变形温度(0.45MPa,未退火) | ISO75-2/B | 220 | °C | ||
| 热变形温度(1.8MPa,未退火) | ISO75-2/A | 200 | °C | ||
| 熔融温度2 | ISO11357-3 | 220 | °C | ||
| 线形热膨胀系数-流动 | ISO11359-2 | 2.0E-5 | cm/cm/°C | ||
| 线形热膨胀系数-横向 | ISO11359-2 | 7.0E-5 | cm/cm/°C | ||
| 电气性能 | 表面电阻率 | IEC60093 | -- | ohms | |
| 体积电阻率 | IEC60093 | 1.0E+15 | ohms·cm | ||
| 介电强度 | IEC60243-1 | 30 | kV/mm | ||
| 相对电容率 | 100Hz | IEC60250 | 3.50 | ||
| 1MHz | IEC60250 | 3.30 | |||
| 耗散因数 | 100Hz | IEC60250 | 5.0E-3 | ||
| 1MHz | IEC60250 | 0.015 | |||
| 漏电起痕指数 | IEC60112 | -- | V | ||
| 可燃性 | FlammabilityClassification | 0.75mm | IEC60695-11-10,-20 | HB | |
| 1.5mm | IEC60695-11-10,-20 | HB | |||
| 灼热丝易燃指数 | 1.5mm | IEC60695-2-12 | 700 | °C | |
| 2.0mm | IEC60695-2-12 | 700 | °C | ||
| 热灯丝点火温度 | 1.5mm | IEC60695-2-13 | 725 | °C | |
| 2.0mm | IEC60695-2-13 | 725 | °C |
用于PA6(聚已内酰胺#尼龙6) | K224-G6U | 荷兰DSM
特性备注:33%玻纤增强生产厂商：荷兰DSM
PA6 | Akulon® K224-G6-FC NA99001 | 荷兰帝斯曼
特性备注:生产厂商：荷兰帝斯曼
PA6 | Akulon® K224-G6 | 荷兰帝斯曼
特性备注:生产厂商：荷兰帝斯曼
PA6 | Akulon® K224-G6U | 荷兰帝斯曼
特性备注:生产厂商：荷兰帝斯曼
PA6 | Akulon® K224-G6-FC BK00001 | 荷兰帝斯曼
特性备注:生产厂商：荷兰帝斯曼
PA6 | Akulon® K224-G6-FC 99.99.99 | 荷兰帝斯曼
特性备注:生产厂商：荷兰帝斯曼